Product Description:
Epoxy low surface treatment paint is a two-component thick-build epoxy resin with low solvent content and high volume solid content. It is suitable for the construction and maintenance of components.
BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating stands as a testament to innovation and excellence in surface protection. This specialized paint formulation harnesses the power of epoxy resin, offering superior durability and performance while minimizing environmental impact.
Key Features of BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating:
Epoxy Paint Performance: Engineered with advanced epoxy resin technology, our paint delivers exceptional adhesion and corrosion resistance, ensuring long-lasting protection for various substrates.
Low Solvent Epoxy: Formulated with reduced solvent content, BGM-30 minimizes VOC emissions and environmental footprint without compromising on performance, making it an eco-friendly choice for coating applications.
High Solid Paint: With a high solid content, our coating provides excellent coverage and film build, resulting in superior protection and aesthetic appeal with fewer coats required.
Versatile Application: Whether for industrial facilities, commercial buildings, or marine structures, BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating offers versatility and adaptability to diverse coating projects.
Enhanced Durability: Trusted by professionals worldwide, our coating withstands the rigors of harsh environments, including abrasion, chemicals, and UV exposure, ensuring long-term protection and performance.
Professional-Grade Quality: Manufactured to the highest industry standards, BGM-30 undergoes rigorous testing and quality control measures to ensure consistent performance and reliability in real-world applications.
In conclusion, BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating stands as a premier choice for surface protection, offering unmatched durability, environmental responsibility, and performance. Trust in our expertise to safeguard your valuable assets and infrastructure for years to come.
For more information on BGM-30 and its applications, please don't hesitate to reach out to us. Our team of experts is here to assist you in finding the perfect solution for your coating needs.
Product Usage:
Can be used on a variety of substrates, including manually treated rusted steel, sandblasted steel, and a variety of intact aged coatings. Provides excellent corrosion protection in the atmosphere and water for industrial, coastal, pulp and paper mills, bridges and offshore installations.
Physical parameters:
Color: aluminum gray, aluminum red
Volume solid content: 80±2%
Standard film thickness: Dry film: 125 microns Wet film: 156 microns
Theoretical coating rate: 4.4㎡/kg 6.4㎡/L (based on 125 micron dry film)
Actual Coverage Rate: Consider Appropriate Loss Factors
Flash point: 28±2℃(after mixing)
Construction Instructions:
Surface Treatment: The performance of this product depends on the degree of surface treatment. All surfaces to be coated should be clean, dry and free of contamination. Prior to painting, all surfaces should be qualified and treated in accordance with ISO 8504:2000 standards. Scale and soluble salts must be removed. Scale buildup can generally be removed with a dry bristle brush, while soluble salts should be rinsed with fresh water. Blast treatment This product must be used on surfaces that have been blast treated to meet Sa2.5 (ISO8501-1:2007) or SSPC-SP10 standards. If used in the atmosphere, this product should be used on surfaces with treatment results that meet at least Sa2.5 (ISO8501-1:2007) or SSPC-SP6 standards for optimal performance. Surface defects exposed during blasting should be ground, filled or treated in an appropriate manner. Recommended surface roughness is 50-75 microns.
Manual or powered processing
Perform manual or power processing to at least meet the standards of St2 (ISO8501-1:2007) or SSPC-SP2. Note: All oxide scale must be removed. Any parts that cannot be adequately treated with a shovel or striker gun should be subject to local blasting treatment to make the surface at least meet Sa2 (ISO8501-1:2007) or SPPC-SP6 standards. Generally speaking, this applies to Class C or D rust standards. Recommended surface roughness is 50-75 microns.
Ultra-high pressure water spray treatment/wet spray treatment
Can be used on surfaces blast treated to Sa2.5 (ISO8501-1:2007) or SSPC-SP6 standards.
Aging coating
This product is suitable for coating on a limited number of aged coatings that are undamaged and have intact adhesion (intact aged alkyd, epoxy and polyurethane coatings). Loose or flaking coatings should be scraped over until a solid layer of paint is exposed. Smooth surfaces require light roughening to create ideal adhesion.
The substrate temperature should not be lower than 10℃, and should be at least 3℃ higher than the air dew point temperature.
Mixing: This product comes in two cans to form one unit. It must be mixed in pairs at one time according to the prescribed ratio every time, and used up within the prescribed mixing period.
(1) Stir the base ingredients (A) with a power mixer
(2) Mix all the curing agent (B) and base material (A) together and stir thoroughly with a power mixer.
Mixing service life:
15℃ | 25℃ | 35℃ |
3H | 2H | 0.5H |
Thinner: JINYU No. 1 Thinner
Construction method: | airless spray | air spray (with pressure tank) | brush/roller |
Dilution ratio: | 0-5% | 5-15% | 5-10% |
Airless spray:
Nozzle size: 0.58-0.79mm
Discharge pressure: 15MPa
Drying time:
(Wet film thickness 156μm, relative humidity 50%) | 15℃ | 25℃ | 35℃ |
Fingers dry to touch | 8H | 4H | 2H |
Transportable | 18H | 10H | 4H |
fully cured | 14 days | 7 days | 3 days |
Recoat interval:
(Wet film thickness 156μm, relative humidity 50%) | 15℃ | 25℃ | 35℃ |
shortest | 18H | 10H | 4H |
Packing specifications: 25KG/group
Product Description:
Epoxy low surface treatment paint is a two-component thick-build epoxy resin with low solvent content and high volume solid content. It is suitable for the construction and maintenance of components.
BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating stands as a testament to innovation and excellence in surface protection. This specialized paint formulation harnesses the power of epoxy resin, offering superior durability and performance while minimizing environmental impact.
Key Features of BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating:
Epoxy Paint Performance: Engineered with advanced epoxy resin technology, our paint delivers exceptional adhesion and corrosion resistance, ensuring long-lasting protection for various substrates.
Low Solvent Epoxy: Formulated with reduced solvent content, BGM-30 minimizes VOC emissions and environmental footprint without compromising on performance, making it an eco-friendly choice for coating applications.
High Solid Paint: With a high solid content, our coating provides excellent coverage and film build, resulting in superior protection and aesthetic appeal with fewer coats required.
Versatile Application: Whether for industrial facilities, commercial buildings, or marine structures, BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating offers versatility and adaptability to diverse coating projects.
Enhanced Durability: Trusted by professionals worldwide, our coating withstands the rigors of harsh environments, including abrasion, chemicals, and UV exposure, ensuring long-term protection and performance.
Professional-Grade Quality: Manufactured to the highest industry standards, BGM-30 undergoes rigorous testing and quality control measures to ensure consistent performance and reliability in real-world applications.
In conclusion, BGM-30 Low Surface Treatment Low Solvent Epoxy Paint High Solid Coating stands as a premier choice for surface protection, offering unmatched durability, environmental responsibility, and performance. Trust in our expertise to safeguard your valuable assets and infrastructure for years to come.
For more information on BGM-30 and its applications, please don't hesitate to reach out to us. Our team of experts is here to assist you in finding the perfect solution for your coating needs.
Product Usage:
Can be used on a variety of substrates, including manually treated rusted steel, sandblasted steel, and a variety of intact aged coatings. Provides excellent corrosion protection in the atmosphere and water for industrial, coastal, pulp and paper mills, bridges and offshore installations.
Physical parameters:
Color: aluminum gray, aluminum red
Volume solid content: 80±2%
Standard film thickness: Dry film: 125 microns Wet film: 156 microns
Theoretical coating rate: 4.4㎡/kg 6.4㎡/L (based on 125 micron dry film)
Actual Coverage Rate: Consider Appropriate Loss Factors
Flash point: 28±2℃(after mixing)
Construction Instructions:
Surface Treatment: The performance of this product depends on the degree of surface treatment. All surfaces to be coated should be clean, dry and free of contamination. Prior to painting, all surfaces should be qualified and treated in accordance with ISO 8504:2000 standards. Scale and soluble salts must be removed. Scale buildup can generally be removed with a dry bristle brush, while soluble salts should be rinsed with fresh water. Blast treatment This product must be used on surfaces that have been blast treated to meet Sa2.5 (ISO8501-1:2007) or SSPC-SP10 standards. If used in the atmosphere, this product should be used on surfaces with treatment results that meet at least Sa2.5 (ISO8501-1:2007) or SSPC-SP6 standards for optimal performance. Surface defects exposed during blasting should be ground, filled or treated in an appropriate manner. Recommended surface roughness is 50-75 microns.
Manual or powered processing
Perform manual or power processing to at least meet the standards of St2 (ISO8501-1:2007) or SSPC-SP2. Note: All oxide scale must be removed. Any parts that cannot be adequately treated with a shovel or striker gun should be subject to local blasting treatment to make the surface at least meet Sa2 (ISO8501-1:2007) or SPPC-SP6 standards. Generally speaking, this applies to Class C or D rust standards. Recommended surface roughness is 50-75 microns.
Ultra-high pressure water spray treatment/wet spray treatment
Can be used on surfaces blast treated to Sa2.5 (ISO8501-1:2007) or SSPC-SP6 standards.
Aging coating
This product is suitable for coating on a limited number of aged coatings that are undamaged and have intact adhesion (intact aged alkyd, epoxy and polyurethane coatings). Loose or flaking coatings should be scraped over until a solid layer of paint is exposed. Smooth surfaces require light roughening to create ideal adhesion.
The substrate temperature should not be lower than 10℃, and should be at least 3℃ higher than the air dew point temperature.
Mixing: This product comes in two cans to form one unit. It must be mixed in pairs at one time according to the prescribed ratio every time, and used up within the prescribed mixing period.
(1) Stir the base ingredients (A) with a power mixer
(2) Mix all the curing agent (B) and base material (A) together and stir thoroughly with a power mixer.
Mixing service life:
15℃ | 25℃ | 35℃ |
3H | 2H | 0.5H |
Thinner: JINYU No. 1 Thinner
Construction method: | airless spray | air spray (with pressure tank) | brush/roller |
Dilution ratio: | 0-5% | 5-15% | 5-10% |
Airless spray:
Nozzle size: 0.58-0.79mm
Discharge pressure: 15MPa
Drying time:
(Wet film thickness 156μm, relative humidity 50%) | 15℃ | 25℃ | 35℃ |
Fingers dry to touch | 8H | 4H | 2H |
Transportable | 18H | 10H | 4H |
fully cured | 14 days | 7 days | 3 days |
Recoat interval:
(Wet film thickness 156μm, relative humidity 50%) | 15℃ | 25℃ | 35℃ |
shortest | 18H | 10H | 4H |
Packing specifications: 25KG/group